Aluminum Sheet / Plate

The advantage properties of aluminum alloy are light weight, excellent electrical and thermal conductivity, high corrosion resistance and ductility. Aluminum alloy is soft and usually alloyed with copper, zinc, magnesium, silicon, manganese and lithium to increase strength. When aluminum alloy is exposed to air, an anti-oxidant coating will be formed instantly to protect products. Aluminum alloy is one of the lightest metals.When aluminum ingot is passed between rolls under pressure, it becomes thinner and longer in the direction in which it is moving. This simple process is the basis for producing aluminum plate, sheet and foil. Sheet, the most widely used form of industrial aluminum, is used in applications including aerospace (the skins of planes), transportation (auto body sheet), packaging (can bodies and ends) and construction (building facades).

 Standard Specification: GB/T 3880, ASTM B209, EN485

Alloy and Temper
AlloyTemper
1xxx:1050,1051A, 1060, 1100O, H12, H14, H16, H18, H22, H24, H26, H112
3xxx:3003, 3004, 3005, 3105O, H12, H14, H16, H18, H22, H24, H26, H112
5xxx:5005, 5052, 5754, 5083O, H22, H24, H26, H28, H32, H34, H36, H38, H111, H112
6xxx:6061, 6082T4, T6, T451, T651
2xxx:2014, 2017,2024T351, T451
7xxx:7075T651

 Size Range

DimensionRange
Thickness0.5 ~ 6.0mm for sheet
6.0 ~ 150mm for plate
Width900 ~ 4000mm
Length2000 ~ 10000mm

  • – Standard Width and Length: 1000x2000mm, 1250x2500mm, 1500x3000mm, 1219x2438mm, 1524x3048mm
    – Surface Finish: Mill finish, unless otherwise specified
    – Surface Protection: Paper interleaved, PE/PVC filming (if required)

 Temper Designation

TemperDefinition
FAs fabricated (no mechanical property limits specified)
OAnnealed
H12Strain Hardened, 1/4 Hard
H14Strain Hardened, 1/2 Hard
H16Strain Hardened, 3/4 Hard
H18Strain Hardened, Full Hard
H111Annealed and slightly strain hardened (less than H11)
H112Slightly strain harden from working at an elevated temperature or from limited amount of cold work
H22Strain Hardened and Partially Annealed, 1/4 Hard
H24Strain Hardened and Partially Annealed, 1/2 Hard
H26Strain Hardened and Partially Annealed, 3/4 Hard
H28Strain Hardened and Partially Annealed, Full Hard
H32Strain Hardened and Stabilized, 1/4 Hard
H34Strain Hardened and Stabilized, 1/2 Hard
H36Strain Hardened and Stabilized, 3/4 Hard
H38Strain Hardened and Stabilized, Full Hard
T351Solution heat-treated, cold worked, stress-relieved by stretching and naturally aged
T4Solution heat-treated and naturally aged
T451Solution heat-treated, stress-relieved by stretching and naturally aged
T6Solution heat-treated and then artificially aged
T651Solution heat-treated, stress-relieved by stretching and artificially aged