3105 Aluminum Alloy Sheet and Coil
3105 Aluminum alloys have high strength at subzero temperatures. They also have high ductility. 3105 Aluminum alloys is 98% pure Aluminum alloy. It has high corrosion resistance, and good weldability and formability. 3105 aluminum alloy has slightly higher strength than 3003 aluminum. Other properties are similar to 3003 aluminum alloy. 3105 aluminium has good anti-rust property, good electrical conductivity which can be as high as 41%. 3105 aluminum sheet has high plasticity in the annealing state.
Forming
Aluminium / Aluminum 3105 alloy has good forming characteristics. It is suggested that bend radii should be used in one thickness to 2 t range for annealed H12, H14 and H16 tempers. Bend radii of 2 to 7 t should be used for the H18 temper.
Welding
Aluminium / Aluminum 3105 alloy has good weldability. It can be welded using arc welding method.
Heat Treatment
Aluminium / Aluminum 3105 alloy does not react to heat treatment except during cold working.
Forging
Aluminium / Aluminum 3105 alloy can be forged at the temperatures ranging from 372 to 510°C (700 to 950°F).
Hot working
Aluminium / Aluminum 3105 alloy can be hot worked at 205 to 372°C (400 to 700°F)
Cold Working
Aluminium / Aluminum 3105 alloy has good cold working characteristics in the harder cold worked tempers.
Annealing
Aluminium / Aluminum 3105 alloy is annealed at 344°C (650°F) followed by cooling in air.
Hardening
Aluminium / Aluminum 3105 alloy can be hardened only by cold working in H12, 14, 16, 18 or 25 tempers.
Applications
Aluminium / Aluminum 3105 alloy is used in sheet metal work. It is also used in manufacturing mobile homes, residential siding, and rain carrying goods.
| Alloy | 3105 |
|---|---|
| Temper | F,O,H12,H14,H16 H18,H19,H22,H24 H26,H28,H111,H112 |
| Thickness | 0.1-250mm |
| Width | <4000mm |
| Length | <12000mm |